Product Features

• Modified UV curable acrylic coating.
• Protects substrates such as aluminum alloys used for smartphone shells during machining. Reduces or avoids cracks or jagged edges. Also provides temporary protection against the weak alkaline solutions used in precision machining.
• Applied via spray coating. Can be completely removed without residue via immersion in ≥ 85 °C water for 5 min under ultrasonic treatment after machining is completed. The protective film floats off the substrate as a complete piece. The water can then be safely disposed of without secondary pollution. This makes it a more environmentally friendly method than other similar temporary protective coatings which use alkaline or acidic solutions.

Product Specifications

Product Number:	7430
Appearance:	Blue translucent liquid
Viscosity (25 °C, Brookfield LVT #4):	4000 ± 1000 cps

 

Applications	Substrates
Protective coating for machining	Aluminum Aluminum alloys Stainless steel Crystal

Recommended Spray Coating Parameters

• Spray solvents: crude toluene : xylene : butyl acetate = 1 : 1 : 1
• Solvent content: 50 ~ 60 %, adjust the viscosity to 10 – 12 s (Iwata #2), and adjust as necessary.
• Pre-baking conditions: 60 °C for 2 – 3 min (confirm solvent is fully volatile)
• Dry film thickness: 15 ~ 20 μm
• Integrated exposure energy: 500 ~ 800 mJ/cm2

Product Package: 3 or 10 kg (in plastic pail)